DUROPOXY ΛΕΥΚΟ

9,42 €
- +

Glue - two component putty in

New

Glue - two component putty in
32 shades without solvents based on epoxy resins and selected quartz aggregates.

Displays unique properties in tile investment of all types, both welding and their grouting.

Has excellent resistance to acids, alkalis, strong cleansers, several organic solvents, the chlorinated and seawater.

It has excellent workability, high adhesion to flanks of the joints, provides impermeability and stain resistant. It is non-absorbent, prevents the growth of bacteria, easy to clean and resistant in strict hygienic conditions.

Provides unbreakable bonding fixed and solid substrates.

It is suitable for grouting joints in back 2-10 mm. Before cure, easily cleaned with EPOXY GROUT CLEANER VIOCLEAN of DUROSTICK.

It is classified as a glue to R2T class by EN 12004 and as putty in the category RG according to EN 13888.



specifications

Form - Colour
A (RESIN) - firm paste
32 shades
B (HARDENER) - Liquid - Honey

Specific gravity of mix


1,65 ± 0,05 kg / lt

Value for mixing


A 12 parts / 1 part B

Pot life


2 hours at 20 ° C, 1 hour at 40 ° C

application temperature


From +10 ° C to +35 ° C

temperature resistance


From -40 ° C to +110 ° C

Foot traffic


After 16 hours at 23 ° C

Shrinkage


null
MECHANICAL PROPERTIES


Resistance 28 days in EN 196-1 at:

• bending


30,00 N / mm²

• grief


63,50 N / mm²

Strength 7 days per DIN 18156 in:

• posting


3,50 N / mm²


APPLICATIONS

The DUROPOXY 32 shades are necessary in areas such as food industries (meat-fish-vegetable-fruit), abattoirs, canning factories, dairy products, wineries, chemical laboratories, pharmaceutical companies, car washes, public toilets, swimming pools, swimming pools, kitchens (fig .1) bathrooms (Fig.2) etc.

It is suitable for horizontal and vertical applications, both indoors and outdoors without trichiazei.



USE

1. Substrate preparation for tiling-application

The cementitious application surfaces should be clean, free from loose parts, dust, grease, oils, paints, etc. If necessary, rub with an electric sander with patocharto No50 or wire brush. In special cases be sandblasted.

Adeiazoume all liquid component B (hardener) to the container by the component (resin).

Stir for about 5 minutes, using a low speed drill until ensure complete homogenization of the two components.

To premix spread and "combed" uniformly on the substrate with a notched trowel.

2. Grouting tile - application

Apomakrynete the joints and tile surface any glue residues and remove dust.

The joints are filled with rubber spatula, spreading and compacting a diagonal to the joints without leaving voids and leftovers.


REMARKS

• loose or cracked cementitious joints, dismantled 3-4mm in depth. After thoroughly clean the sides of the tiles and remove dust, fill with DUROPOXY, above.

• The pools ambient temperature + 20 ° C and above can be used after 2 days and less than + 20 ° C, after 4 days.

• Epoxy systems are sensitive to temperature and humidity of the environment until the complete hardening. H elevated temperature results in the reduction of the mix life while the high humidity the occurrence of blurred or discolored spots on the surface and increase the final cure time. After mixing the two components increase of temperature of the mixture.

• To product after hardening, they are harmless to health and the environment.


consumption


For bonding: about 1,75 kg / m² / mm
For grouting: 0,2-3,0 kg / m2

LIST TELL CONSUMPTIONS JOINTING

TILE DIMENSIONS


WIDTH JOINTS

(In cm)


2mm


3mm


4mm


5mm


7mm


10mm

2 x 2 x 0,3


1,020


1,500


0


0


0


0

4,2 x 4,2 x 0,6


980


1,450


1,950


2,600


3,050


4390

10 x 10 x 0,6


400


600


800


1,020


0


0

15 x 15 x 0,7


310


460


620


790


0


0

20 x 30 x 0,7


200


300


400


500


0


0

30 x 30 x 0,8


180


280


370


450


550


0

40 x 40 x 0,8


0


190


280


350


440


630

50 x 50 x 0,8


0


150


240


310


350


500

(Consumer prices calculated in gr / m²)


CHEMICAL RESISTANCE OF CERAMIC TILE spliced ​​DUROPOXY

NAME


CONCENTRATION


ABSORPTION%


REMARKS

Lactic acid


10%


2.6


no impact

Sulfuric acid


10%


3.6


no impact

Sulfuric acid


50%


2.1


Discoloration

Nitric acid


10%


3.1


no impact

Acetic acid


10%


6.4


no impact

Hydrochloric acid


10%


1.9


slight discoloration

Hydrochloric acid


37%


6.5


Discoloration

phosphoric acid


10%


2.5


slight discoloration

Ammonia


10%


2.4


no impact

Sodium hydroxide


10%


1.3


no impact

sodium hypochlorite


10%


1.6


no impact

light oil


-


0.5


no impact

ethanol


15%


1.7


no impact

ethanol


96%


7.7


no impact

Ethanol + Acetic acid


(15% -3%)


2.6


no impact

MIBK


-


2.1


no impact

xylene


-


0.9


no impact

 

The samples were cured at room temperature for 10 days and then
immersed in the above chemical reagents for 30 days at 25 ° C.